Flaxseed gum (FG)-based films were developed with the addition of glycerol as a plasticizer and glutaraldehyde as a crosslinking agent. HCl was added to improve crosslinking and decrease the hydrophilicity of the matrix. Different cellulose nanocrystal (CN) amounts were used as reinforcements in the optimum FG formulation. The crosslinking process at pH 3.5 led to a lower solubility of FG in water (from 100% to 53%) and an increase in thermal stability (from 160 ºC to 209 ºC). FTIR analysis confirmed a reduction in the -OH band due to crosslinking between the hydroxyl groups of FG. A diffuse diffraction pattern was observed for all FG films. The addition of 4% w/w of CN contributed to reduction of water solubility (from 53% to 20.8%) and absorption (from 21.9% to 6.8%). Finally, an improvement was observed in the tensile mechanical properties in the nanocomposites, showing satisfactory results for the proposed formulations, mainly with 8% w/w of CN added to the matrix. Overall, this study demonstrated that FG/CN nanocomposites are promising materials to be use as a sustainable biopolymer for application as bioplastics.

Abstract This study evaluated the effects of the incorporation of a new additive to asphalt cement oil (CAP). A polyol product was obtained through the oxypropylation reaction of sugarcane bagasse. This polyol was polymerised with pyromellitic anhydride in order to obtain a polyester (BCP) to test its suitability in terms of the material properties to be applied as additives. FTIR spectra of the polymerised material (BCP) confirmed the occurrence of chemical modification due to the appearance of a new band at 1750 cm-1, characteristic of ester groups. The TGA data showed that the BCP product had higher thermal stability than the polyol. According to the softening point and elastic recovery tests, the incorporation of 11% and 16% w/w BCP in conventional CAP met the specifications of regulatory standards.

In this work, the effects of incorporating cellulose nanocrystals from soy hulls (WSH30) on the mechanical, thermal, and barrier properties of methylcellulose (MC) nanocomposites were evaluated. MC/WSH30 nanocomposite films with different filler levels (2, 4, 6, 8, and 10%) were prepared by casting. Compared to neat MC film, improvements in the mechanical and barrier properties were observed, while thermal stability was retained. The improved mechanical properties of nanocomposites prepared may be attributed to mechanical percolation of WSH30, formation of a continuous network of WSH30 linked by hydrogen interactions and a close association between filler and matrix.